Hybrid Silica-Phytic Acid Coatings: Effect on the Thermal Stability and Flame Retardancy of Cotton
| Autoři | |
|---|---|
| Rok publikování | 2019 |
| Druh | Článek v odborném periodiku |
| Časopis / Zdroj | POLYMERS |
| Fakulta / Pracoviště MU | |
| Citace | |
| www | https://www.mdpi.com/2073-4360/11/10/1664/htm |
| Doi | http://dx.doi.org/10.3390/polym11101664 |
| Klíčová slova | sol-gel processes; flame retardancy; cotton; phytic acid; solid state NMR spectroscopy; thermal stability; durability |
| Popis | New hybrid sol-gel coatings based on tetraethoxysilane (TEOS) and phytic acid (PA) were designed and applied to cotton; the flame-retardant properties of the treated fabrics were thoroughly investigated by means of flame-spread and forced-combustion tests. The first goal was to identify the TEOS:PA weight ratio that allowed the achievement of the best flame-retardant properties, with the lowest final dry add-on on the fabrics. Therefore, different TEOS:PA sols were prepared and applied to cotton, and the resulting coated fabrics were thoroughly investigated. In particular, solid-state NMR spectroscopy was exploited for assessing the condensation degree during the sol-gel process, even for evaluating the occurrence of possible reactions between phytic acid and the cellulosic substrate or the alkoxy precursor. It was found that a total dry add-on of 16 wt % together with 70:30 TEOS:PA weight ratio provided cotton with self-extinction, as clearly indicated by flame-spread tests. This formulation was further investigated in forced-combustion tests: a significant reduction of heat release rate (HRR), of the peak of HRR, and of total heat release (THR) was found, together with a remarkable increase of the residues after the test. Unfortunately, the treated fabrics were not resistant to washing cycles, as they significantly lost their flame-retardant properties, consequently to the partial removal of the deposited hybrid coatings. |