Early hydration of C4AF with silica fume and its role on katoite composition
| Autoři | |
|---|---|
| Rok publikování | 2024 |
| Druh | Článek v odborném periodiku |
| Časopis / Zdroj | Journal of Microscopy |
| Fakulta / Pracoviště MU | |
| Citace | |
| www | https://onlinelibrary.wiley.com/doi/10.1111/jmi.13280 |
| Doi | http://dx.doi.org/10.1111/jmi.13280 |
| Klíčová slova | C(4)AF; hydration; katoite; microstructure; silica fume |
| Popis | 4AF is considered the least reactive main clinker phase, but its reactivity may be affected by adding supplementary cementitious materials (SCMs). Pure C4AF was synthesised in a laboratory furnace, and the role of silica fume without gypsum on its early hydration properties was monitored. Burning was carried out in four stages to achieve 99% purity of C4AF. Heat flow development was monitored by isothermal calorimetry over 7 days of hydration at 20°C and 40°C. The role of silica fume on hydrogarnet phase katoite (Ca3Al2(SiO4)3 – x(OH)4x x = 1.5–3) formation during early hydration was studied. Rapid dissolution of C4AF, formation of metastable C-(A,F)-H and its conversion to C3(A, F)H6 was evidenced by isothermal calorimetry as a large exotherm. Changes in microstructure during early hydration were documented by SE micrographs, EDS point analyses, X-ray mapping and line scans by SEM-EDS. The phase composition was characterised by DTA-TGA and QXRD after 7 days of hydration. The katoite diffraction pattern is similar for the reference sample and sample with silica fume, but substitution in its structure can be revealed by X-ray microanalyses. The composition of katoite is variable due to the various extent of substitution of 4OH- by SiO44- due to silica fume. |