Characterization of sintered Ag nanopowder joints using nanoindentation tests

Autoři

BURŠÍK Jiří SOPOUŠEK Jiří BURŠÍKOVÁ Vilma STÝSKALÍK Aleš ŠKODA David

Rok publikování 2011
Druh Článek v odborném periodiku
Časopis / Zdroj Chem. listy
Fakulta / Pracoviště MU

Přírodovědecká fakulta

Citace
Obor Fyzika plazmatu a výboje v plynech
Klíčová slova Nanoindentation; Silver nanopowder; Solder
Popis Sandwiches consisting of copper disks with Ag nanopowder interlayer annealed at various temperatures from 200 to 350 C were studied. The main emphasis was placed on the characterization of quality of the sintered Ag layers by means of nanoindentation experiments. The highest hardness values were obtained after annealing at 350 C. The highest values of the Young's modulus were achieved after annealing at 250 C, indicating the lowest porosity of the sintered layer.